Superconducting 123YBaCu-oxide produced at low temperatures

ABSTRACT

A method of preparing a superconductor. The method includes preparing a mixture of superconductor material constituents, disposing the constituents on a silver containing substrate, heating the mixture of constituents on a silver containing substrate, heating the mixture in a first atmosphere having a partial pressure of CO 2  to control decomposition of at least one of the superconductor material constituents and changing the first atmosphere to a second atmosphere consisting essentially of an oxidizing gas capable of allowing decomposition of at least one of the superconductor material constituents.

This invention was developed at least in part under U.S. Air Force Contract F19628-91-C-0082, and the U.S. government has certain rights in this invention pursuant to this contract.

BACKGROUND OF THE INVENTION

The present invention relates generally to a superconductor material. More particularly, the invention relates to a textured, high temperature superconductor ceramic ("HTSC") material and a method of producing this material at low temperatures.

High temperature superconducting ceramics (HTSC) are intrinsically weak and brittle materials. In addition, conventional ceramic processing of these materials produces polycrystalline bodies which have low critical current densities (j_(c), in DC measurements) and high surface resistivities (R_(s), in RF measurements). Commercial applications of these materials require components that exhibit high j_(c) and/or low R_(s) values as well as the capability of producing mechanically strong and easy to manufacture components. Due to the materials' low mechanical strength, commercially useful structures cannot be produced without the use of a substrate to impart strength and toughness to the superconductor. This is especially true for lower frequency RF devices that will require the superconductor to be formed into relatively large, complex shapes. HTSC thin films have been shown to have high current densities and low R_(s) values. However, these films are not useful for low frequency RF applications because they require expensive single crystal substrates (typically, LaAlO₄ or SrTiO₄) and can only be formed into planar structures with dimensions under a few inches.

Bulk HTSC materials with highly textured microstructures can exhibit the level of electrical performance required for commercial applications. For YBa₂ Cu₃ O_(7-x), such textured microstructures are produced using a method called peritectic recrystallization or, more commonly, "melt-texturing". In this process, "textured" YBa₂ Cu₃ O_(7-x) is produced by crystallizing this compound out of its peritectic mixture of Y₂ BaCuO₅ plus a Ba/Cu-rich liquid. Many variations of this technique have been described, and it is commonly practiced in laboratories throughout the world. However, the process remains essentially the same as that originally developed in 1988.

The melt-texturing process typically involves heating a sample above the peritectic temperature (1015° C. in air) to decompose the YBa₂ Cu₃ O_(7-x) into Y₂ BaCuO₅ plus liquid. This mixture is cooled slowly through the peritectic temperature allowing YBa₂ Cu₃ O_(7-x) to crystallize. When this cooling is performed in the presence of a thermal gradient, the YBa₂ Cu₃ O_(7-x) grains preferentially grow parallel to the gradient and a "textured" microstructure results. The slow cooling keeps the nucleation rate of YBa₂ Cu₃ O_(7-x) low, resulting in the formation of a small number of nuclei. As a result, the YBa₂ Cu₃ O_(7-x) grains can grow to very large sizes before impingement; and if the cooling is performed in a thermal gradient, the grains will be highly aligned. In the originally developed process samples were measured to have critical currents of up to 17,000 A/cm² in self-field with only a small magnetic field dependence. Improvements to this process (which have included the production of continuous lengths of melt-textured filaments) have resulted in measured current densities as high as 140,000 A/cm² in self field and 44,000 A/cm² in a 1 Tesla field at 77 K.

While the melt-texturing process has proven to be very effective in the fabrication of bulk YBa₂ Cu₃ O_(7-x) having properties approaching those of thin film materials, it has substantial drawbacks. First, melt-texturing is essentially a crystal growth process in which the rate of material production is controlled by the velocity of the crystallization front. In the case of YBa₂ Cu₃ O_(7-x) crystallizing out of its peritectic mixture, the crystallization rate is extremely sluggish. Even in extremely large thermal gradients (10⁷ K/m) growth rates of only 1.2 cm/hr have been achieved. A second problem, of particular importance to texturing thick film structures, is the fact that the melt-texturing process requires processing at temperatures above 1000° C. in the presence of the extremely reactive peritectic liquid. This severely limits the choice of substrate materials that can be used without reacting with the superconductor. To date, only zirconia and magnesia have been used with any degree of success, and these ceramics are expensive and difficult to process.

It is therefore an object of the invention to provide an improved method of producing a high temperature superconductor (HTSC) material.

It is a further object of the invention to provide a novel method of producing an HTSC material at relatively low temperatures with very high rate of production.

It is another object of the invention to provide an improved method of producing HTSC structures on relatively inexpensive substrates.

It is yet a further object of the invention to provide a novel HTSC article of manufacture.

It is still an additional object of the invention to provide an improved method of manufacturing HTSC material and an article of manufacture having relatively intricate patterns formed directly from the process.

It is still another object of the invention to provide a novel HTSC article of manufacture of an intermediate phase state having minimal liquid involved in its manufacture.

Further objects and advantages of the present invention, together with the organization and manner of operation thereof, will become apparent from the following detailed description of the invention when taken in conjunction with the accompanying drawings, wherein like elements have like numerals throughout the drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 illustrates a 40× magnification microstructure of reactively textured YBa₂ Cu₃ O_(7-X) on silver buffered stainless steel;

FIG. 2 shows a reactively textured YBa₂ Cu₃ O_(7-x) on a silver substrate at 40× magnification;

FIG. 3 illustrates a conventional peritectic recrystallized thick film microstructure on a zirconia substrate;

FIG. 4A illustrates an exemplary rocking angle X-ray diffraction curve showing the highly textured nature of an HTSC material prepared by one of the methods of the invention; and FIG. 4B shows X-ray diffraction patterns for three crystalline YBa₂ Cu₃ O_(7-x) samples;

FIG. 5 illsutrates a pseudobinary phase diagram of Y₂ BaCuO₂ and 3Ba0.5CuO; and

FIG. 6 shows surface RF resistivity extrapolated to 1 GHz for YBa₂ Cu₃ O_(7-x) specimens of the invention, a prior art sintered YBa₂ Cu₃ O_(7-x) and Cu.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

A process in accordance with one form of the invention involves the crystallization of YBa₂ Cu₃ O_(7-x) out of a metastable liquid formed by rapidly introducing a non-equilibrium mixture of Y-, Ba-and Cu-compounds (mixed in the appropriate stoichiometry) into a combination of temperature and a gas atmosphere in which YBa₂ Cu₃ O_(7-x) is the thermodynamically stable phase. Two general variations of this process have been successfully demonstrated. In the first general method of preparation, Y₂ O₃, CuO, and BaCO₃ powders are mixed in a molar ratio of 0.5:3.0:2.0 and are heated in a CO₂ rich atmosphere to approximately 850° C. to 890° C. The atmosphere is then changed to 2 torr of pure oxygen. The use of a CO₂ -rich atmosphere during heating suppresses the decomposition of BaCO₃ and consequently prevents YBa₂ Cu₃ O_(7-x) from forming prematurely. When the atmosphere is rapidly changed to a reduced pressure oxygen environment, the reaction mixture begins to decompose to a partially molten state out of which YBa₂ Cu₃ O_(7-x) crystallizes.

In a second general method of preparation, a prereacted, phase-pure YBa₂ Cu₃ O_(7-x) powder is heated to approximately 850° C. to 890° C., also in a CO₂ -rich atmosphere. Without limiting the scope of the invention, it is believed the presence of the CO₂ causes the YBa₂ Cu₃ O_(7-x) to decompose into a complex mixture of oxides and oxycarbonates. As for the first general method, the atmosphere is changed at temperature to a reduced pressure oxygen containing atmosphere, which causes this mixture to decompose into the partially molten state from which YBa₂ Cu₃ O_(7-x) can crystallize.

In accordance with one form of the invention, this `reactive texturing` process is preferably carded out on either a silver foil or a base metal, such as a stainless steel, which has been electroplated with either silver or silver with a nickel intermediate layer. In this embodiment the silver or silver/nickel buffer layers are necessary since YBa₂ Cu₃ O_(7-x) and its precursors are relatively active compounds which react strongly with most base metals. Silver is relatively inert with respect to YBa₂ Cu₃ O_(7-x). This silver or silver/nickel buffer layer is preferably at least 0.002" thick to protect the superconductor. Base metals which have proven satisfactory include stainless steels, such as 302 stainless steel, 304 stainless steel, 316 stainless steel and also Inconel 600. The process has been practiced on a variety of shapes, including discs, tubes, wires and coils. Copper can also be used in this temperature range. The successful use of copper as a substrate requires use of an appropriate intermediate metal which will prevent interdiffusion of copper, silver and oxygen.

The substrate can be coated with the precursor slurry of appropriate stoichiometry using either painting, dipping, spraying, or any other technique currently used to apply thick film coatings or patterns. It has been determined that the preferred thickness of this applied coating is about 0.002" to 0.008". The preferred thermal processing has three steps:

1. Binder/organic removal. Heating of the coating is preferably carried out in a reduced total pressure oxygen environment (e.g., 2 torr of oxygen) heated at a rate of between 30° C./hr and 300° C./hr from room temperature to a temperature between 350° C. and 500° C. which is sufficient to removal the volatile components of the precursor paint.

2. Reaction suppression/precursor formation. Heating of the coating is preferably performed at a rate of about 300° C./hr. in a nitrogen atmosphere containing between at least about 0.8% and 2.8% CO₂. One can use higher pressures of CO₂, but such higher pressures are more than needed to suppress the decomposition of BaCO₃ or initiate the decomposition of YBa₂ Cu₃ O_(7-x). The CO₂ can be mixed with any inert gas, such as N₂, argon or helium. The temperature is preferably between the temperature of the binder removal stage and the temperature of the crystallization stage. These temperatures are sufficient to suppress the formation of YBa₂ Cu₃ O_(7-x) in the case of an oxide/carbonate precursor or decompose the YBa₂ Cu₃ O_(7-x) precursor to an appropriate mixture of oxides and oxycarbonates.

3. Crystallization. A preferred window for crystallization of YBa₂ Cu₃ O_(7-x) exists between about 850° C. and 900° C. in an atmosphere of about 1 to 3 torr of oxygen, although the oxygen pressure can range up to one atmosphere pressure. Below about 850° C., the grain sizes are greatly reduced in size. It should also be noted that at higher oxygen partial pressures, the process temperature increases such that at 0.21 atm. oxygen the temperature of treatment would be about 975° C. Preferably the process temperature is maintained below the melting point of the silver containing substrate. Most preferably, therefore, the pressure of oxygen is kept below about 50 torr to operate at a temperature below 925° C. (the melting point of silver at 50 torr). One can choose to perform the process by slowly increasing the temperature within this window during the crystallization process as opposed to using a simple isothermal hold. Either procedure is acceptable.

In the above described preferred process an intermediate product, or article of manufacture, is obtained. In the conventional melt texturing process the peritectic zone (region P in FIG. 5) encompasses the region of the phase diagram involved in producing the desired YBa₂ Cu₃ O_(7-x). In this conventional method the amount of liquid present is quite large throughout the processing temperature range (about 1015° C. then cooled slowly through the peritectic temperature of 1013 ° C.). On the other hand in the instant invention, rather than having an intermediate product of solid material and a substantial percentage of peritectic liquid, the intermediate product is primarily a solid and a small fraction of a eutectic liquid (not a peritectic liquid). Since the reactants are metastable, the liquid that forms is the lowest melting liquid in the Y-Ba-Cu-O system, that is, the ternary eutectic. Substantial advantages result from being able to prepare textured YBa₂ Cu₃ O_(7-x) without excess liquid present. One such advantage is the ability to cast well defined solid patterns without need of liquid barriers in place. A desired pattern can be disposed on a substrate, such as by applying a thick film slurry in a desired pattern; and then the YBa₂ Cu₃ O_(7-x) can be formed by the method of the invention without substantial liquid flowage causing loss of the shape of the desired pattern. Thus, the intermediate product of the invention formed at about 850°-900° C. does not have the undesirable large liquid component present in the conventional intermediate product formed in the peritectic region.

A process has been described herein which produces textured YBa₂ Cu₃ O_(7-x) microstructures, as in the peritectic recrystallization method. However, unlike peritectic recrystallization, the instant method produces these microstructures at low temperatures (less than about 900° C.) and in relatively short times (less than about 1 hr compared to 10-15 hours for conventional melt texturing). This combination of low temperatures and short times enables the use of relatively inexpensive and easy to form base metal substrates that substantially reduce the potential cost of the component. This cost reduction makes this process much more attractive for the commercial application of HTSC components. This process is especially attractive for the fabrication of three dimensional RF resonant structures which are the fundamental components of numerous RF devices such as filters, oscillators and combiners. As can be seen in FIG. 6, the resulting YBa₂ Cu₃ O_(7-x) exhibits a substantially improved RF resistivity over both conventional copper and over a prior art YBa₂ Cu₃ O_(7-x) prepared by sintering and disposed on a silver substrate.

The following are nonlimiting examples of methods of preparing HTSC materials.

EXAMPLE 1

A mixture of Y₂ O₃, CuO, and BaCO₃ was mixed in turn with an acrylic binder, a sorbitan trioleate dispersant, and an n-butanol/xylene solvent to make precursor `paint`. Other suitable carder formulations can also be used as understood in the art. This paint was then applied to a silver foil using a paint brush. The resultant dried coating was 0.008" thick. This sample was then placed in a controlled atmosphere furnace, heated in 2 torr of oxygen at 60° C./hr to 350° C. to insure adequate removal of the organic components of the paint. The atmosphere of the furnace was then changed to 0.9% CO₂ in nitrogen, and the sample was heated to 900° C. at a rate of about 300° C./hr. The atmosphere of the furnace was again changed to 2 torr of oxygen, and the sample was held at temperature for 1 hour. This treatment resulted in a textured, crystallized YBa₂ Cu₃ O_(7-x) microstructure.

EXAMPLE 2

A commercial YBa₂ Cu₃ O_(7-x) powder was mixed with an acrylic binder, a sorbitan trioleate dispersant, and an n-butanol/xylene solvent to make a precursor `paint`. This paint was applied to a 304 stainless steel disc, a 316 stainless steel disc, and an Inconel 600 disc (all 1.125" diameter and previously electroplated with 0.002" of silver) with a paint brush. The resultant dried coating was, in all cases, about 0.004 to 0.005" thick. All three samples were then placed in a controlled atmosphere furnace, and heated in 2 torr of oxygen at 60° C./hr to 350° C. to insure proper removal of the organic components of the paint. The atmosphere of the furnace was then changed to 1.1% CO₂ in nitrogen, and the sample was heated to 880° C. at a rate of 300° C./hr. The atmosphere of the furnace was again changed to 2 torr of oxygen, and the furnace temperature was slowly increased at a rate of 25° C./hr to 900° C. This treatment resulted in a textured, crystallized YBa₂ Cu₃ O_(7-x) microstructure for all samples.

EXAMPLE 3

A variety of starting materials different from those used in Examples 1 and 2 also proved satisfactory. These starting materials included: (1) phase pure YBa₂ Cu₃ O_(7-x) with 22% Y₂ BaCuO₅, (2) YBaSrCu₃ O_(7-x) with 22% Y₂ BaCuO₅, (3) a CuO rich commercially available YBa₂ Cu₃ O_(7-x) and stoichiometric YBa₂ Cu₃ O_(7-x). All of these starting materials were used successfully in implementing the methods described in Examples 1 and 2.

EXAMPLE 4

Any one of the above example procedures was followed and the pattern of the original starting material remained substantially the same after preparing YBa₂ Cu₃ O_(7-x). This was compared to conventionally prepared YBa₂ Cu₃ O_(7-x) (peritectic processing) which showed substantial liquid flowage and loss of the spatial pattern of the original starting material. 

What is claimed is:
 1. A method of preparing a 123 YBaCu-oxide superconductor, comprising the steps of:preparing a mixture of superconductor material constituents for the 123 YBaCu-oxide superconductor; disposing said constituents on a silver containing substrate; heating said mixture to a temperature between about 350° C.-975° C. in a first atmosphere having a partial pressure of CO₂ corresponding to at least about 0.8% by volume CO₂ ; and controlling decomposition of at least one of said superconductor material constituents thereby suppressing decomposition of BaCO₃, as well as enabling decomposition and suppressing formation of 123 YBaCu-oxide precursor and changing said first atmosphere to a second atmosphere consisting essentially of an oxidizing gas capable of allowing decomposition of at least one of said superconductor material constituents and heating said superconductor material constituents to form the 123 YBaCu-oxide superconductor.
 2. The method as defined in claim 1 wherein said first atmosphere consists essentially of a carbon dioxide-containing gas.
 3. The method as defined in claim 1 wherein said mixture of superconductor material constituents comprises a pre-reacted single phase 123 YBaCu-oxide product.
 4. The method as defined in claim 1 wherein said second atmosphere comprises about 1 torr to 1 atmosphere of oxygen gas.
 5. The method as defined in claim 4 wherein said oxygen gas comprises at least about 1-3 torr pressure of oxygen.
 6. The method as defined in claim 1, wherein said superconductor material constituents comprise at least one of (a) a mixture of Y₂ O₃, CuO and BaCO₃ (b) single phase 123 YBaCu-oxide with 22% Y₂ BaCuO₅, (c) YBaSrCu₃ O_(7-x) with 22% Y₂ BaCuO₅, (d) CuO rich 123 YBaCu-oxide and (e) 123 YBaCu-oxide powders.
 7. The method as defined in claim 6 wherein said superconductor material constituents of group (a) are mixed in a molar ratio of about 0.5:3.0:2.0.
 8. The method as defined in claim 1 wherein said first and second atmosphere include an inert gas.
 9. A method of preparing an intermediate product having a well-defined substantially solid pattern in a pseudobinary system of Y₂ BaCuO₂ /3Ba0.5CuO, comprising the steps of:providing starting constituents capable of yielding a 123 YBaCu-oxide heating said starting constituents to a temperature between about 350° C.-975° C. in a CO₂ containing atmosphere; and heating further said starting constituents to a temperature range between about 850° C.-975° C. in an oxidizing atmosphere to form said intermediate product having said well defined solid pattern without substantial liquid flowage characteristics in said temperature range.
 10. The method as defined in claim 9 wherein said CO₂ containing atmosphere comprises an inert gas and at least about 0.8-2.8% by volume CO₂.
 11. The method as defined in claim 9 wherein said oxidizing atmosphere comprises at least about 1 torr of oxygen.
 12. The method as defined in claim 9 further including the step of heating said starting constituents to a temperature of about 350° C.-500° C. to drive off binder/organic volatiles.
 13. The method as defined in claim 9 further including the step of disposing said starting constituents on a substrate selected from the group consisting of silver and a base metal.
 14. The method as defined in claim 13 wherein said base metal is selected from the group consisting of stainless steel and Inconel.
 15. The method as defined in claim 9 wherein said solid pattern comprises a thick film slurry which is disposed on a substrate.
 16. A method of preparing a 123 YBaCu-oxide superconductor, comprising the steps of:(a) preparing a mixture of superconductor material constituents capable of forming a 123 YBaCu-oxide superconductor; (b) disposing said superconductor material constituents on a substrate; (c) heating said mixture to a temperature between about 350° C.-975° C. in a first atmosphere having a partial pressure of CO₂ corresponding to at least about 0.8% by volume CO₂, thereby suppressing decomposition of BaCO₃, decomposing any 123 YBaCu-oxide precursor to a mixture of oxides and oxycarbonates and suppressing formation of 123 YBaCu-oxides; and (d) changing said first atmosphere to a second atmosphere comprising an oxidizing gas capable of allowing decomposition of at least one of said superconductor material constituents, said oxidizing gas having an equivalent oxygen partial pressure ranging from at least one torr oxygen to about one atmosphere oxygen and heating said superconductor material constituents to form the 123 YBaCu-oxide superconductor.
 17. The method as defined in claim 17 wherein said substrate is selected from the group consisting of a buffered base metal and silver.
 18. The method as defined in claim 17 wherein said equivalent oxygen partial pressure in step (d) ranges from about 1 torr to about 0.21 torr and the temperature of heating in step (d) ranges from about 850° C. to 975° C. 